DURABILITY AND CORROSION BEHAVIOR OF Ni-Cr-Al DETONATION COATINGS UNDER Na₂SO₄/NaCl EXPOSURE

This study investigates the durability and corrosion resistance of Ni-Cr-Al detonation-sprayed coatings when exposed to high-temperature environments containing molten Na₂SO₄ and NaCl. Such conditions are highly corrosive and frequently encountered in aerospace, energy, and chemical industries. Gradient and homogeneous Ni-Cr-Al coatings were compared to understand their behavior under aggressive exposure. The reveal of results those gradient coatings exhibit superior corrosion resistance due to their ability to retain protective oxides, such as Cr₂O₃, and mitigate stress-induced damage through compositional grading. In contrast, homogeneous coatings displayed significant degradation, including widespread corrosion, delamination, and the formation of sodium-based phases like NaNiO₂. XRD analysis confirmed the presence of oxidation and sulfidation products, with gradient coatings showing enhanced stability against phase transitions. These findings highlight the potential of gradient Ni-Cr-Al coatings to improve component performance in extreme conditions and provide valuable insights for optimizing coating compositions and processes to enhance operational reliability in harsh environments.

1. A comprehensive study on hot corrosion resistance of NiCoCrAlYTa and NiCrAl thermal-sprayed coatings for CSP applications / А. Daniel et al // Journal of Energy Storage. – 2023. – V. 74. – Р. 109346.

2. Comparative hot corrosion performance of APS and Detonation sprayed CoCrAlY, NiCoCrAlY and NiCr coatings on T91 boiler steel / C. Sundersan et al // Corrosion Science. – 2021. – V. 189. – Р. 109556.

3. Manjor K. Production of Nanocrystalline Ni-20Cr Coatings for High-Temperature Applications / K. Manjor, S. Harpreet, S. Narinder // Journal of Thermal Spray Technology. – 2014. – V. 23. – Р. 692-707.

4. Structure and Tribological Properties of Ni-Cr-Al Based Gradient Coating Prepared by Detonation Spraying / В. Rakhadilov et al // Coatings. – 2021. – Vol. 11(2). – P. 218.

5. Sukhpal S.C. High temperature hot corrosion behaviour of NiCr and Cr3C2-NiCr coatings on T91 boiler steel in an aggressive environment at 750°C / S.C. Sukhpal, S.S. Hazoor, S.S. Buta // Surface and Coatings Technology. – 2012. – V. 206(19). – Р. 3839-3850.

6. Madjid S. Corrosion of steel alloys in eutectic NaCl+Na2CO3 at 700 °C and Li2CO3 + K2CO3 + Na2CO3 at 450°C for thermal energy storage / S. Madjid, A. Theodore, W. Geoffery // Solar Energy Materials and Solar Cells. – 2017. – Vol. 170. – P. 48-59.

7. Niraj B. Accelerated hot corrosion studies of cold spray Ni–50Cr coating on boiler steels / В. Niraj, S. Harpreet, P. Satya // Materials & Design. – 2010. – Vol. 31(1). – P. 244-253.

8. Lina M. Comparative review of different influence factors on molten salt corrosion characteristics for thermal energy storage / M. Lina, Zh. Cancan, W. Yuting // Solar Energy Materials and Solar Cells. – 2022. – Vol. 235. – P. 111485.

9. Xin R. High-temperature oxidation and hot corrosion behaviors of the NiCr–CrAl coating on a nickel-based superalloy / R. Xin, W. Fuhui, W. Xin // Surface and Coatings Technology. – 2005. – Vol. 198(1). – P. 425-431.

10. Investigation of high-temperature oxidation of homogeneous and gradient Ni-Cr-Al coatings obtained by detonation spraying / B. Rakhadilov et al // Coatings. – 2024. – Vol. 14(11). – P. 1-11.